Product information
Metric Internal Retaining Ring / circlip for bore DIN472/D1300/DHO/J
Carbon Spring Steel is the standard material for these internal retaining rings, and phosphate & Oil are the standard finishes. Stainless steel rings is made from SS420, SS304 or SS316.
Company Introduction
Oriental Industry Co., Ltd is a leading manufacturer of retaining rings, circlips, snap rings, disc Spring washers, spring pins etc. in China. Our factory has obtained IATF16949 and ISO14001 certificates. The products can be applied to automotive industry, wind power machinery, engineering machinery, electrical tool, electrical appliance, general machinery etc. 80% of our products are exported to Europe, North America, South America and Asian & Pacific area. By introducing advanced equipment, using quality material and develop new process, Oriental Industry has set up a well-established production system. The utilization rate of raw material is improved from 30% to 70%. We have invested the advanced cold rolling mill which ensures the thickness tolerance within 0.05 mm.
Material:
Carbon spring steel C67S, 60Si2Mn, Stainless Steel SS420, SS304, SS316.
Workshop:
Products
1 Retaining rings, circlips, snap rings, E rings, DIN471, DIN472, DIN6799, DIN983,DIN984, D1300, D1400, D1460, D1500, CRESCENT RING (M1800), GRIP RING
2 Russian standard retaining rings, GOST 13942, GOST 13943,ГОСТ 13942, ГОСТ 13943
3 Snap rings, Retaining spring flat concentric rings, GOST 13940, GOST 13941, ГОСТ 13940, ГОСТ 13941, DIN5417/M3200/SP series, WRE, WR-SW(M2400) Series, BR-AR-SB, M2300 SB Series, DIN7993 round wire rings
4 Spring pins, DIN1481 / ISO8752, DIN7346 / ISO13337
Material: carbon spring steel 65Mn, SUS304
Finish: blackened, galvanized
5 DIN2093, DIN6796 Disc springs, conical spring washer
6 DIN6798A, B, J DIN lock washers
7 DIN137 wave spring washers
8 DIN128 split lock washer, curved spring lock washer
9 We also provide custom-made retaining rings and stamped products. All the tooling will be made on our own expense within 3 days.
10 Grease nipples
11 Hose clamps
Certificates
Heat treatment and finish
- Austempering is applied to increase the mechanical property of our products. Our modern heat treatment equipment and skillful technicians guarantee each retaining ring within the mechanical properties required.
- The standard finish of carbon steel retaining rings is phosphate.
- Dacromet is available on request.
- Zinc plating is available, but is not recommended because of the risk of hydrogen brittleness.
- Stainless steel is polished into original color after heat treatment.
Chemical and mechanical properties of steel
Carbon spring steel C67 EN 10132-4: 2000
Chemical components of Carbon spring steel C67S
C | Si | Mn | P | S | Ni | Cr | Mo | Cu | other |
0.65-0.73 | 0.15-0.35 | 0.60-0.90 | ≤0.025 | ≤0.025 | ≤0.400 | ≤0.400 | ≤0.100 | - |
Mechanical properties of C67S
Condition of delivery | Soft annealed (+A) or soft annealed and slightly rerolled (+LC) | Quenched and tempered (+QT) |
0,2% proof stress Rp0,2 [N/mm²] | max. 510 | 1200 - 1900 |
Tensile strength Rm [N/mm²] | max. 640 | |
Fracture elongation A80 [%] | min. 16 | |
Hardness [HV] | max. 200 | 370 - 580 |
Hardness [HRB] | max. 92 | |
Hardness [HRC] | 38,5 - 54 |
Typical hardness values (HV) for quenched and tempered materials at different thickness ranges
Effective thickness [mm] | 0,30<=0,50 | 0,50<=0,75 | 0,75<=1,00 | 1,00<=1,50 | 1,50<=2,00 | 2,00<=3,00 |
Hardness [HV] | 485 - 535 | 465 - 515 | 455 - 505 | 445 - 495 | 425 - 475 | 415 - 465 |
Stainless Steel SS420
2Cr13, which is equivalent to 420, is frequently used for SS retaining rings. The hardness reaches HRC 44-50 after heat treatment. This makes our SS retaining rings much excel the just 'stamped stainless retaining rings'
Chemical composition (%) of 2Cr13
C | Si | Mn | P | S | Ni | Cr | Mo | Cu | other |
0.16-0.25 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.030 | * | 12.00-14.00 | - | - | - |
Steel 60Si2Mn
Chemicals :
C | Si | Mn | P | S | Ni | Cr | Mo | Cu | other |
0.57~0.65 | 1.50~2.00 | 0.60~0.90 | ≤0.035 | ≤0.035 | ≤0.35 | ≤0.35 | - | -≤0.25 | - |
Mechanical Property:
Tensile Strength: σb (MPa):≥1274(130)
Yield strength σs (MPa):≥1176(120)
Elongation δ10 (%):≥5
reduction of cross section ψ (%):≥25
Hardness :hot rolling,≤321HB; cold rolling+heat treatment,≤321HB